PrimaCreator Value Flex UV 3D printer resin 500 ml - black

All about the product

Black "Flex" line "PrimaCreator" resin, designed for 3D printers. Cured by UV rays with a wavelength of 395 nm to 405 nm. Models obtained after printing are flexible, showing very low shrinkage. The vulcanized resin has high impact strength - from 65 to 75 D Shore hardness scale. The finished models need to be cleaned from resin residues with isopropyl alcohol (IPA). The product is sold in a 500 ml bottle.

"PrimaCreator" resin properties

• Finished prints have a uniform color with a semi-matte surface.
• The highest quality components are used for resin production
• To remove resin residues from the printed model, use isopropyl alcohol (IPA)
• Designed primarily for DLP printers with a lower power UV light source used to improve the resin, including "Zortrax Inkspire" and "Anycubic Photon"
• Prints prepared from the resin show high hardness - Shore scale from 65 to 75 D
• Curing time depends on the resin color and ranges from 4 to 12 seconds per layer
• The finished models can be dried in a special UV chamber for 2 to 5 minutes. They can also be dried in sunlight, the print should be exposed to UV rays for 10 to 20 minutes. With little sunlight, this time extends to 60 minutes.

Specification:

• Elastic modulus: from 1,882 to 2,385 MPa
• Flexural strength: from 40 to 70 MPa
• Deformation temperature: 80 ° C
• Thermal expansion: 95 E-6
• Shrinkage value: from 3.72% to 4.24%
• Linear shrinkage: from 1.05% to 1.35%
• Tensile strength: from 30 to 52 MPa
• Tensile modulus: from 1,779 to 2,385 MPa
• Hardness: from 65 to 75 D.
• Stiffness temperature: 100 ° C
• Density: from 1.05 to 1.25 g / cm3
• Impact: from 41 to 48 j / m
• Viscosity: from 1050 to 300 MPa x s
• Curing time: from 4 to 12 s for 0.005 mm layer
• UV wavelength of the vulcanizing resin: from 395 to 405 nm