PrimaCreator Value Flex UV Resin - 500ml - Light Grey
59.00 €
Ikm. maksa no 2,42 €
3563615 PV-RF-B405-0500-LG
7340002117539
Piegāde 11-18 d.d.
Šī prece Jūs ieinteresēja
Viss par produktu
PrimaCreator Value Flex Resin is a good quality resin made from the best raw materials. It offers good quality resin 3D prints. Cure the 3D prints in sunlight or in a UV curing chamber. Once the curing is complete, you will get flexible 3D prints with very little shrinkage. The objects have a very smooth surface.Take advantage of good quality resin 3D printing at a low price. Flexible resin is the perfect resin when you are looking for highly detailed results that need to be highly impact resistant. A hardness of 65-75 D shore and an incredible elongation of 130% make it a resin that can be used in many areas.
After printing, clean the 3D print with IPA (isopropyl alcohol) to wash away any resin left on the model.
When it comes time to cure, you can use sunlight or a UV curing chamber. Depending on the print, curing times can vary: in a UV curing chamber it will take about 2-5 minutes. In the sun it will take 10-20 minutes. In daylight on a cloudy day it can take up to 60 minutes.
If you want amazing results at a lower price than many other brands – PrimaCreator VALUE resin should be your first choice. Buy now!
Main features:
- Shore hardness 65–75 D and elongation at break 130%
- 3D printed parts are highly impact resistant
- 3D print flexible objects with very low shrinkage
- Optimized for UV light source 395-405 nm
- Works great on low-power DLP 3D printers
- Fast curing time, 4-12 (depending on color) seconds per coat
- Flexural modulus: 1.882 - 2.385 MPa
- Bending strength: 40-70 MPa
- Hot deformation temp.: 80℃
- Thermal expansion: 95/E-6
- Volume shrinkage: 3.72 - 4.24%
- Linear shrinkage: 1.05 - 1.35%
- Tensile strength: 30 - 52 MPa
- Tensile modulus: 1.779 - 2.385 MPa
- Elongation at break: 130%
- Hardness (Shore D): 65 - 75D
- Glass transition temperature: 100 ℃
- Density: 1.05-1.25 g/cm3
- Notch impact strength: 41-48 j/m
- Viscosity: 150-300 MPa
- Curing time: 4 - 12s, with a layer thickness of 0.05 mm; bottom layer 40 - 60s